Eastman Tritan MP100 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Film and sheet manufactured from this new-generation copolyester can be thermoformed with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan MP100 copolyester is suitable for use with most forms of sterilization including radiation and ethylene oxide. It is not suitable for autoclave/steam sterilization. Eastman Tritan MP100 has been formulated for use in medical film, sheet, and packaging applications.

Application/Uses

• Device packaging

• Extruded medical films and sheeting

• Medical articles from sheet

• Rigid medical packaging

• Sterile medical packaging

Key Attributes

• Good toughness

• Does not contain Bisphenol-A (BPA)

• Does not contain plasticizers

• Enduring sustainability

• Excellent heat resistance

• Outstanding chemical resistance

• Reliable, predictable processing for extrusion, thermoforming, heat and radio frequency sealing

• Suitable for most forms of sterilization

• Good, long-term clarity

PCTG TRITAN MP100

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in3	ASTM D1505
Water Absorption	0.50 %@Time 86400 sec	0.50 %@Time 24.0 hour	ASTM D570
Water Vapor Transmission	4.00 g/m2/day@Temperature 23.0 °C	0.258 g/100 in2/day@Temperature 73.4 °F	ASTM F1249
	11.0 g/m2/day@Temperature 38.0 °C	0.708 g/100 in2/day@Temperature 100 °F	ASTM F1249
Oxygen Transmission	32.0 cc-mm/m2-24hr-atm	81.3 cc-mil/100 in2-24hr-atm	ASTM D3985
Carbon Dioxide Transmission	149 cc-mm/m2-24hr-atm	378 cc-mil/100 in2-24hr-atm	ASTM D1434
Thickness	250 microns	9.84 mil	Thickness of film tested; ASTM D374
Surface Tension	45 dynes/cm	45 dynes/cm	Polar; ASTM D5946
Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	41.0 MPa	5950 psi	ASTM D882
Film Tensile Strength at Yield, TD	40.0 MPa	5800 psi	ASTM D882
Film Elongation at Break, MD	179 %	179 %	ASTM D882
Film Elongation at Break, TD	203 %	203 %	ASTM D882
Film Elongation at Yield, MD	7.0 %	7.0 %	ASTM D882
Film Elongation at Yield, TD	7.0 %	7.0 %	ASTM D882
Secant Modulus, MD	1.462 GPa	212.0 ksi	ASTM D882
Secant Modulus, TD	1.383 GPa	200.6 ksi	ASTM D882
Puncture Energy	4.60 J@Temperature 23.0 °C	3.39 ft-lb@Temperature 73.4 °F	Dynatup; ASTM D3763

PCTG TRITAN MP100

PCTG 一种透明塑料，是一种非晶型共聚酯，PCTG常用的共聚单体为1,4-环己烷二甲醇(CHDM)，全称为聚对苯二甲酸-1,4-环己烷二甲醇酯。它是由对苯二甲酸(PTA)、乙二醇(EG)和1,4-环己烷二甲醇(CHDM)三种单体用酯交换法缩聚的产物，与PET比较多了1,4-环己烷二甲醇共聚单体，与PCT比多了乙二醇共聚单体，因此，PCTG的性能和PET、PCT大不相同。 PCTG是一种非结晶型共聚聚酯，随着共聚物中CHDM的增加，熔点下降，玻璃化温度上升，结晶度下降， 形成无定形聚合物。PCTG中CHDM的含量大于50%。

PCTG用途:

板、片材:

使用常规的成型方法，可以制备1~25.4mm厚的透明材料，具有突出的韧性和高抗冲击强度，其抗冲击强度是改性聚丙烯酸酯类的3~10倍，成型性能优异，冷弯曲不泛白，无裂纹，易于印刷和修饰，广泛应用于室内外标牌、储物架、自动售货机面板、家具、建筑及机械挡板等。

PCTG卡主要应用于欧洲，但在北美、亚洲也得到了越来越多的应用。原因是具有很宽的加工范围，高的机械强度和优异的柔性，比起PVC透明度高，光泽好，容易印刷并且具有环保优势。

PCTG材料应用于。Visa公司是 上 的公司之一，1998年其 卡片发行量为5.8亿张。该公司已认可二醇类改性聚酯(PCTG)为其材料。对于要求卡片材料对环境更友好的国家，PETG可替代聚氯乙烯材料。Visa还指出：来自3个不同试验厂的结果显示，PCTG满足国际标准(150/IEC7810)的所有要求，因此PCTG卡片在这里可能得到广泛使用。

异型材:

可成型管材或各种型材，其制品坚硬、透明、光泽好，受压不泛白，易于成型及后加工处理，符合环保要求，同时符合美国FDA关于食品接触标准，广泛应用于建筑装饰及材料。

膜用：专门应用于高性能收缩膜，有大干70%的最终收缩率，可制成复杂外形容器的包装，具有高吸塑力，高透明度，高光泽，低雾度，易于印刷，不易脱落，存储时自然收缩率低的优点，应用于饮料瓶、食品和化；陵品的收缩包装及电子产品等的收缩标签。其中双向拉伸的。PETG膜适用于高档包装、印刷、电子电器、电缆包扎、绝缘材料以及各种工业领域的 基材。单向拉伸PET、热收缩薄膜适用于各种罐装，聚酯瓶、各种容器等外用标签。与PVC收缩膜相比，PETG收缩膜还具有环保的优点。

PCTG TRITAN MP100 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格 ，质量保证！