东丽耐湿热30%玻纤PPS Torelina A673M-T
|
Density (23°C) |
1.52 |
g/cm3 |
ISO 1183 |
|
Molding Shrinkage 2 |
Internal Method | ||
|
Across Flow : 3.00 mm |
0.85 |
% |
|
|
Flow : 3.00 mm |
0.20 |
% |
|
|
Water Absorption (24 hr, 23°C) |
0.020 |
% |
ISO 62 |
| Hardness |
Nominal Value |
Unit |
Test Method |
|
Rockwell Hardness (R-Scale) |
114 |
ISO 2039-2 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Stress (23°C) |
150 |
MPa |
ISO 527-2 |
|
Tensile Strain (Break, 23°C) |
2.5 |
% |
ISO 527-2 |
|
Flexural Modulus (23°C) |
10000 |
MPa |
ISO 178 |
|
Flexural Stress (23°C) |
225 |
MPa |
ISO 178 |
|
Shear Strength (23°C) |
68.0 |
MPa |
JIS K7214 |
|
Taber Abrasion Resistance (1000 Cycles) |
50.0 |
mg |
ISO 9352 |
|
Coefficient of Friction - vs. Metal |
0.25 |
||
| Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength (23°C) |
14 |
kJ/m2 |
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C) |
60 |
kJ/m2 |
ISO 179 |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Heat Deflection Temperature (1.8 MPa, Unannealed) |
255 |
°C |
ISO 75-2/A |
|
Melting Temperature |
278 |
°C |
ISO 11357-3 |
|
CLTE |
ISO 11359-2 | ||
|
Flow |
2.2E-5 |
cm/cm/°C |
|
|
Transverse |
3.3E-5 |
cm/cm/°C |
| Electrical |
Nominal Value |
Unit |
Test Method |
|
Volume Resistivity |
1.0E+14 |
ohms·cm |
IEC 60093 |
|
Electric Strength |
26 |
kV/mm |
IEC 60243-1 |
|
Dielectric Constant (23°C, 1 MHz) |
3.80 |
IEC 60250 | |
|
Dissipation Factor (23°C, 1 MHz) |
2.0E-3 |
IEC 60250 | |
| Flammability |
Nominal Value |
Unit |
Test Method |
|
Flame Rating (1.5 mm) |
V-0 |
UL 94 |