日本三菱食品挤出级PC Iupilon E-2001R
|
Density |
1.20 |
g/cm3 |
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) |
5.3 |
g/10 min |
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) |
5.00 |
cm3/10min |
ISO 1133 |
|
Tensile Modulus |
2400 |
MPa |
ISO 527-2/1 |
|
Tensile Stress (Yield) |
60.0 |
MPa |
ISO 527-2/50 |
|
Tensile Strain |
ISO 527-2/50 | ||
|
Yield |
5.4 |
% |
|
|
Break |
110 |
% |
|
|
Flexural Modulus 3 |
2300 |
MPa |
ISO 178 |
|
Flexural Stress 3 |
93.0 |
MPa |
ISO 178 |
| Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength (23°C) |
88 |
kJ/m2 |
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C) |
No Break |
ISO 179 |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Heat Deflection Temperature |
|||
|
0.45 MPa, Unannealed |
145 |
°C |
ISO 75-2/B |
|
1.8 MPa, Unannealed |
131 |
°C |
ISO 75-2/A |
PC在室温下具有相当大的强迫高弹形变能力。冲击韧性高，因此可进行冷压，冷拉，冷辊压等冷成型加工。挤出用PC分子量应大于3万，要采用渐变压缩型螺杆，长径比1：18~24，压缩比1：2.5，可采用挤出吹塑，注-吹、注-拉-吹法成型高质量，高透明瓶子。