PC/1004R/沙伯基础 物性表
|
PROPERTIES
|
|
TYPICAL VALUES
|
UNITS
|
TEST METHODS
|
|
MECHANICAL
|
|
|
|
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
1)
|
63
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
|
6
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
|
>70
|
%
|
ASTM D 638
|
|
Tensile Modulus, 50 mm/min
|
|
2350
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
|
90
|
MPa
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
|
2300
|
MPa
|
ASTM D 790
|
|
Hardness, Rockwell R
|
|
120
|
-
|
ASTM D 785
|
|
Tensile Stress, yield, 50 mm/min
|
|
63
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
|
6
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
|
>70
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
|
2350
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
|
90
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
|
2300
|
MPa
|
ISO 178
|
|
Hardness, Rockwell R
|
|
120
|
-
|
ISO 2039-2
|
|
IMPACT
|
|
|
|
|
|
Izod Impact, unnotched, 23°C
|
|
NB
|
J/m
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
|
800
|
J/m
|
ASTM D 256
|
|
Instrumented Impact Energy @ peak, 23°C
|
|
65
|
J
|
ASTM D 3763
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched 80*10*3 -30°C
|
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*3 +23°C
|
|
70
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*3 -30°C
|
|
12
|
kJ/m2
|
ISO 180/1A
|
|
THERMAL
|
|
|
|
|
|
Vicat Softening Temp, Rate B/50
|
|
143
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 3.2 mm
|
|
138
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 3.2 mm
|
|
127
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 95°C, flow
|
|
7.E-05
|
1/°C
|
ASTM E 831
|
|
Thermal Conductivity
|
|
0.2
|
W/m-°C
|
ASTM C177
|
|
Thermal Conductivity
|
|
0.2
|
W/m-°C
|
ISO 8302
|
|
CTE, 23°C to 80°C, flow
|
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
|
Passes
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate B/50
|
|
143
|
°C
|
ISO 306
|
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
|
138
|
°C
|
ISO 75/Bf
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
|
127
|
°C
|
ISO 75/Af
|
|
PHYSICAL
|
|
|
|
|
|
Specific Gravity
|
|
1.2
|
-
|
ASTM D 792
|
|
Water Absorption, equilibrium, 23C
|
|
0.35
|
%
|
ASTM D 570
|
|
Mold Shrinkage on Tensile Bar, flow
|
|
0.5-0.7
|
%
|
SABIC method
|
|
Mold Shrinkage, flow, 3.2 mm
|
2)
|
0.5-0.7
|
%
|
SABIC method
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
|
10
|
g/10 min
|
ASTM D 1238
|
|
Density
|
|
1.2
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
|
0.35
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 300°C/1.2 kg
|
|
9
|
cm3/10 min
|
ISO 1133
|
|
OPTICAL
|
|
|
|
|
|
Light Transmission, 2.54 mm
|
|
88-90
|
%
|
ASTM D 1003
|
|
Haze, 2.54 mm
|
|
<0.8
|
%
|
ASTM D 1003
|
|
Refractive Index
|
|
1.586
|
-
|
ASTM D542
|
|
Refractive Index
|
|
1.586
|
-
|
ISO 489
|
|
ELECTRICAL
|
|
|
|
|
|
Volume Resistivity
|
|
>1.E+15
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, 1.6 mm
|
|
27
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 60 Hz
|
|
3
|
-
|
ASTM D 150
|
|
Relative Permittivity, 1 MHz
|
|
3
|
-
|
ASTM D 150
|
|
Dissipation Factor, 60 Hz
|
|
0.001
|
-
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz
|
|
0.01
|
-
|
ASTM D 150
|
|
Volume Resistivity
|
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Dielectric Strength, 1.6 mm
|
|
27
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity, 60 Hz
|
|
3
|
-
|
IEC 60250
|
|
Relative Permittivity, 1 MHz
|
|
3
|
-
|
IEC 60250
|
|
Dissipation Factor, 60 Hz
|
|
0.001
|
-
|
IEC 60250
|
|
Dissipation Factor, 1 MHz
|
|
0.01
|
-
|
IEC 60250
|
|
FLAME CHARACTERISTICS
|
|
|
|
|
|
UL Recognized, 94V-2 Flame Class Rating
|
3)
|
1.6
|
mm
|
UL 94
|
|
Injection Molding
|
|
|
|
|
|
Drying Temperature
|
|
120
|
°C
|
|
|
Drying Time
|
|
2-4
|
hrs
|
|
|
Maximum Moisture Content
|
|
0.02
|
%
|
|
|
Melt Temperature
|
|
280-310
|
°C
|
|
|
Nozzle Temperature
|
|
270-290
|
°C
|
|
|
Front - Zone 3 Temperature
|
|
280-310
|
°C
|
|
|
Middle - Zone 2 Temperature
|
|
270-290
|
°C
|
|
|
Rear - Zone 1 Temperature
|
|
260-280
|
°C
|
|
|
Hopper Temperature
|
|
60-80
|
°C
|
|
|
Mold Temperature
|
|
80-110
|