美国SABIC汽车透镜PC LEXAN ALS02

ALS02 resin is a medium-high flow (MFR23), heat and UV stabilized, polycarbonate product with mold release designed for use in the automotive lens market.

Density / Specific Gravity	1.20	g/cm3	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)	23	g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)	21	cm3/10min	ISO 1133

Tensile Modulus
-- 2	2350	MPa	ASTM D638
--	2300	MPa	ISO 527-2/1
Tensile Strength
Yield 3	63.0	MPa	ASTM D638
Yield	63.0	MPa	ISO 527-2/50

Notched Izod Impact
23°C	640	J/m	ASTM D256
-30°C 7	12	kJ/m2	ISO 180/1A
23°C 7	65	kJ/m2	ISO 180/1A

Deflection Temperature Under Load
0.45 MPa, Unannealed, 3.20 mm	133	°C	ASTM D648
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	133	°C	ISO 75-2/Bf

Flame Rating (1.6 mm, Testing by SABIC)

V-2

UL 94