代理科思创182度PC APEC 1897抗紫外
|
Density (23°C) |
1.15 |
g/cm3 |
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) |
19 |
g/10 min |
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (330°C/2.16 kg) |
18 |
cm3/10min |
ISO 1133 |
|
Molding Shrinkage 3 |
ISO 294-4 | ||
|
Across Flow : 2.00 mm |
0.85 |
% |
|
|
Flow : 2.00 mm |
0.85 |
% |
|
Tensile Modulus (23°C) |
2450 |
MPa |
ISO 527-2/1 |
|
Tensile Stress (Yield, 23°C) |
74.0 |
MPa |
ISO 527-2/50 |
|
Tensile Strain (Yield, 23°C) |
6.6 |
% |
ISO 527-2/50 |
|
Nominal Tensile Strain at Break (23°C) |
> 50 |
% |
ISO 527-2/50 |
|
Flexural Modulus 4 (23°C) |
2450 |
MPa |
ISO 178 |
|
Flexural Stress 4 (23°C) |
108 |
MPa |
ISO 178 |
|
Heat Deflection Temperature |
|||
|
0.45 MPa, Unannealed |
172 |
°C |
ISO 75-2/B |
|
1.8 MPa, Unannealed |
157 |
°C |
ISO 75-2/A |
|
Vicat Softening Temperature |
182 |
°C |
ISO 306/B120 |
|
Heat Deflection Temperature |
|||
|
0.45 MPa, Unannealed |
172 |
°C |
ISO 75-2/B |
|
1.8 MPa, Unannealed |
157 |
°C |
ISO 75-2/A |
|
Vicat Softening Temperature |
182 |
°C |
ISO 306/B120 |