吹塑级TPU Estane 2355-95AEF

Density / Specific Gravity	1.22	g/cm3	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/8.7 kg)	13	g/10 min	ASTM D1238
Molding Shrinkage			ASTM D955
Flow	0.50 to 0.90	%
Across Flow	0.60 to 0.90	%
Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	94		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Taber Abrasion Resistance (1000 g, H-22 Wheel)	4.00	mg	ASTM D1044
Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
50% Strain, 3.20 mm	8.30	MPa
Strain, 3.20 mm	9.70	MPa
300% Strain, 3.20 mm	21.4	MPa
Tensile Strength (Break, 3.20 mm)	38.9	MPa	ASTM D412
Tensile Elongation (Break, 3.20 mm)	450	%	ASTM D412
Elongation Set After Break (3.20 mm)	60	%	ASTM D412
Tear Strength 1 (3.20 mm)	105	kN/m	ASTM D624
Compression Set			ASTM D395B
25°C, 22 hr	30	%
70°C, 22 hr	80	%

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	-15.0	°C	DSC
Vicat Softening Temperature	80.6	°C	ASTM D1525 2
CLTE - Flow	1.5E-4	cm/cm/°C	ASTM D696

Injection	Nominal Value	Unit
Drying Temperature	88 to 104	°C
Mold Temperature	16 to 60	°C
Injection Notes