代理韩国乐天PC/ABS Infino LI-1000C
|
Density / Specific Gravity (Natural) |
1.20 |
g/cm3 |
ASTM D792, ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) |
30 |
g/10 min |
ASTM D1238, ISO 1133 |
|
Molding Shrinkage |
ASTM D955 | ||
|
Flow : 3.20 mm |
0.51 to 0.62 |
% |
|
|
Across Flow : 3.20 mm |
0.53 to 0.64 |
% |
|
| Hardness |
Nominal Value |
Unit |
Test Method |
|
Rockwell Hardness (R-Scale) |
117 |
ASTM D785, ISO 2039-2 |
|
Charpy Notched Impact Strength 6 (23°C) |
39 |
kJ/m2 |
ISO 179/1eA |
|
Notched Izod Impact |
|||
|
23°C, 3.18 mm |
640 |
J/m |
ASTM D256 |
|
23°C, 6.35 mm |
550 |
J/m |
ASTM D256 |
|
23°C 6 |
36 |
kJ/m2 |
ISO 180/1A |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Deflection Temperature Under Load |
|||
|
0.45 MPa, Unannealed, 6.40 mm |
142 |
°C |
ASTM D648 |
|
0.45 MPa, Unannealed, 4.00 mm |
138 |
°C |
ISO 75-2/B |
|
0.45 MPa, Annealed, 4.00 mm |
138 |
°C |
ISO 75-2/B |
|
1.8 MPa, Unannealed, 6.40 mm |
132 |
°C |
ASTM D648 |
|
1.8 MPa, Unannealed, 4.00 mm |
122 |
°C |
ISO 75-2/A |
|
1.8 MPa, Annealed, 4.00 mm |
123 |
°C |
ISO 75-2/A |
|
Vicat Softening Temperature |
143 |
°C |
ISO 306/B50 |