Density / Specific Gravity (Natural)

1.29

g/cm3

Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)

34

g/10 min

Molding Shrinkage

Flow : 3.20 mm

0.20 to 0.40

%

Across Flow : 3.20 mm

0.20 to 0.40

%

Nominal Value

Unit

Test Method

Rockwell Hardness (R-Scale)

110

Nominal Value

Unit

Test Method

Tensile Modulus 3

3300

MPa

Tensile Strength 3

Yield

63.0

MPa

Break

63.0

MPa

Tensile Elongation 3 (Break)

6.0

%

Flexural Modulus 4

3900

MPa

Flexural Strength 4

92.0

MPa

Nominal Value

Unit

Test Method

Notched Izod Impact

23°C, 3.18 mm

49

J/m

23°C, 6.35 mm

49

J/m

Nominal Value

Unit

Test Method

Deflection Temperature Under Load

0.45 MPa, Unannealed, 6.40 mm

90.0

°C

1.8 MPa, Unannealed, 6.40 mm

85.0

°C

Vicat Softening Temperature

98.0

°C

Nominal Value

Test Method

Flame Rating

1.2 mm

V-0

3.0 mm

V-0