巴斯夫热稳定耐冲击PA6 Ultramid B3ZG7 SC

Ultramid B3ZG7 SC is an uncolored, 35% glass reinforced, heat stabilized, impact modified PA6 injection molding grade.

Filler / Reinforcement	Glass Fiber, 35% Filler by Weight
Additive	Heat StabilizerImpact Modifier
Features	Heat StabilizedImpact ModifiedOil Resistant
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.37	g/cm3	ISO 1183
Melt Volume-Flow Rate (MVR) (235°C/5.0 kg)	3.00	cm3/10min	ISO 1133
Water Absorption			ISO 62
Saturation, 23°C	6.0	%
Equilibrium, 23°C, 50% RH	1.8	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	10000	MPa	ISO 527-2
Tensile Stress (Break, 23°C)	169	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	4.0	%	ISO 527-2
Flexural Modulus (23°C)	9200	MPa	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179
-30°C	17	kJ/m2
23°C	22	kJ/m2
Charpy Unnotched Impact Strength			ISO 179
-30°C	110	kJ/m2
23°C	100	kJ/m2
Notched Izod Impact Strength			ISO 180
-40°C	17	kJ/m2
23°C	23	kJ/m2

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	219	°C	ISO 75-2/B
1.8 MPa, Unannealed	205	°C	ISO 75-2/A
Melting Temperature (DSC)	218	°C