原包德国朗盛低翘曲PA6 Durethan BG30FN05玻璃珠30%

C	Molding shrinkage, parallel	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0,8
C	Molding shrinkage, transverse	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0,8
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.2
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.2
Mechanical properties (23 °C/50 % r. h.)
C	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	5400	2100
C	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	75	30
C	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.2	>20
C	Charpy impact strength	23 °C	kJ/m2	ISO 179-1eU	40	60
C	Charpy impact strength	-30 °C	kJ/m2	ISO 179-1eU	38	25
C	Charpy notched impact strength	23 °C	kJ/m2	ISO 179-1eA	<10	<10
C	Charpy notched impact strength	-30 °C	kJ/m2	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m2	ISO 180-1U	30	45
	Izod impact strength	-30 °C	kJ/m2	ISO 180-1U	30	20
	Izod notched impact strength	23 °C	kJ/m2	ISO 180-1A	<10	<10
	Izod notched impact strength	-30 °C	kJ/m2	ISO 180-1A	<10	<10

C	Burning behavior UL 94	1.5 mm	Class	UL 94	V-0
C	Burning behavior UL 94	0.4 mm	Class	UL 94	V-0
	Burning behavior UL 94	0.75 mm	Class	UL 94	V-0
	Burning behavior UL 94	3.0 mm	Class	UL 94	V-0