Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 5 mm/min

90

MPa

ASTM D 638

Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 5 mm/min

2.6

%

ASTM D 638

Tensile Modulus / 拉伸模量, 5 mm/min

6200

MPa

ASTM D 638

Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span

160

MPa

ASTM D 790

Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span

5800

MPa

ASTM D 790

Hardness，Rockwell / 洛氏硬度 L

106

–

ASTM D 785

Tensile Stress, break / 抗张程度,断裂, 5 mm/min

97

MPa

ISO 527

Tensile Strain, break / 拉伸伸长,断裂, 5 mm/min

2.5

%

ISO 527

Tensile Modulus / 拉伸模量, 1 mm/min

7070

MPa

ISO 527

Flexural Stress, yield / 弯曲强度,屈服, 2 mm/min

167

MPa

ISO 178

Flexural Modulus / 挠曲模量, 2 mm/min

6540

MPa

ISO 178

Izod Impact, unnotched / 无缺口悬臂梁冲击, 23°C

650

J/m

ASTM D 4812

Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C

119

J/m

ASTM D 256

Izod Impact, notched / 悬臂梁缺口冲击强度, -40°C

96

J/m

ASTM D 256

Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C

22

J

ASTM D 3763

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 +23°C

11

kJ/m2

ISO 180/1A

Charpy Impact, notched /简支梁缺口冲击强度, 23°C

11

kJ/m2

ISO 179/2C

HDT（热变形温度）, 0.45 MPa, 3.2 mm, unannealed （未退火）

140

°C

ASTM D 648

HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火）

135

°C

ASTM D 648

HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）

143

°C

ASTM D 648

HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）

137

°C

ASTM D 648

CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）

2.89E-05

1/°C

ASTM E 831

CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）

8.26E-05

1/°C

ASTM E 831

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

143

°C

ISO 306

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/120

146

°C

ISO 306

HDT（热变形温度）/Be, 0.45MPa Edgew 120*10*4 sp=100mm

143

°C

ISO 75/Be

HDT（热变形温度）/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm

137

°C

ISO 75/Ae

Relative Temp Index, Elec / 相对热指数， 电性能

90

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

90

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

90

°C

UL 746B

Specific Gravity / 比重

1.2

–

ASTM D 792

Water Absorption / 吸水率, 24 hours

0.06

%

ASTM D 570

Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm

0.2 – 0.5

%

SABIC Method

Melt Flow Rate / 熔流率,, 300°C/5.0 kgf

9

g/10 min

ASTM D 1238

Melt Volume Rate / 溶化体积流率, MVR at 300°C/5.0 kg

8

cm3/10 min

ISO 1133

Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm

16.5

kV/mm

ASTM D 149

Relative Permittivity / 相对介电常数, 50/60 Hz

2.86

–

ASTM D 150

Dissipation Factor / 耗散因素, 50/60 Hz

0.0008

–

ASTM D 150