美国沙比克无卤阻燃PPE/PS NORYL SE1X
PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V1, UL746C F1. Dielectric strength. Suitable for E/E market indoor/outdoor applications.
|
Density / Specific Gravity |
1.10 |
g/cm3 |
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) |
8.5 |
g/10 min |
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) |
8.00 |
cm3/10min |
ISO 1133 |
|
Molding Shrinkage |
Internal Method | ||
|
Across Flow 2 |
0.50 to 0.70 |
% |
|
|
Flow : 3.20 mm |
0.50 to 0.70 |
% |
|
|
Water Absorption (24 hr) |
0.060 |
% |
ASTM D570 |
|
Outdoor Suitability |
f1 |
UL 746C |
|
Notched Izod Impact |
|||
|
-30°C |
110 |
J/m |
ASTM D256 |
|
23°C |
180 |
J/m |
ASTM D256 |
|
23°C 9 |
14 |
kJ/m2 |
ISO 180/1A |
|
Unnotched Izod Impact (23°C) |
2600 |
J/m |
ASTM D4812 |
|
Instrumented Dart Impact (23°C, Total Energy) |
49.0 |
J |
ASTM D3763 |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Deflection Temperature Under Load |
|||
|
0.45 MPa, Unannealed, 3.20 mm |
126 |
°C |
ASTM D648 |
|
0.45 MPa, Unannealed, 6.40 mm |
126 |
°C |
ASTM D648 |
|
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 10 |
129 |
°C |
ISO 75-2/Be |
|
1.8 MPa, Unannealed, 3.20 mm |
112 |
°C |
ASTM D648 |
|
1.8 MPa, Unannealed, 6.40 mm |
118 |
°C |
ASTM D648 |
PPO材料作为 五大通用工程塑料之一， ，相对密度小，（PPO/PA同类产品也仅为1.10-1.13g/cm3），是五大通用工程塑料中密度 小的,具有良好的机械强度，抗蠕变性，耐应力松弛，强度高。
PPO/PS合金耐热性突出，热变形温度在1.82MPa下，可以从75-170℃连续变化，随着PPO含量增加，材料的热变汽车工业形温度不断升高，用于满足不同场合的性能需求。PPO及其合金可以采用注塑、挤出、模压、发泡和电镀、真空镀膜、印刷机加工等各种加工方法。