沙伯基础玻纤7%阻燃PPE/PS NORYL PX2906

NORYL PX2906 is a 7% glass reinforced. UL94 V-1 rated resin with a halogen free flame retardant.

Density / Specific Gravity	1.13	g/cm3	ASTM D792
Molding Shrinkage - Flow (3.20 mm)	0.50 to 0.70	%	Internal Method
Water Absorption (24 hr)	0.010	%	ASTM D570
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (L-Scale)	102		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength 2 (Break)	68.0	MPa	ASTM D638
Tensile Elongation 2 (Break)	5.0	%	ASTM D638
Flexural Modulus 3 (50.0 mm Span)	3500	MPa	ASTM D790
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-30°C	77	J/m
23°C	93	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm)	124	°C	ASTM D648
Vicat Softening Temperature	136	°C	ASTM D1525 4
RTI Elec	110	°C	UL 746
RTI Imp	105	°C	UL 746
RTI Str	110	°C	UL 746

PPO性能

   1、PPO综合性能良好，可在120度蒸汽中使用，电绝缘性好，吸水小，但有应力开裂倾向。改性聚苯醚可消除应力开裂。

  2、有突出的电绝缘性和耐水性 ，有较好的 性和电性能，尺寸稳定性好。其介电性能居塑料的首位。

  3、MPPO为PPO与HIPS共混制得的改性材料，市面上的材料均为此种材料。

  4、PPO有较高的耐热性，玻璃化温度211度，熔点268度，加热至330度有分解倾向，PPO的含量越高其耐热性越好，热变形温度可达190度。

  5、PPO阻燃性良好，具有自息性，与HIPS混合后具有中等可燃性。质轻， 可用于食品和 行业。耐光性差，长时间在阳光下使用会变色。