无卤阻燃导电PPE/PA NORYL GTX678

Density / Specific Gravity	1.12	g/cm3	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) (300°C/5.0 kg)	7.8	g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (300°C/5.0 kg)	7.00	cm3/10min	ISO 1133
Molding Shrinkage - Flow (3.20 mm)	1.3 to 1.5	%	Internal Method
Water Absorption			ISO 62
Saturation, 23°C	4.0	%
Equilibrium, 23°C, 50% RH	0.50	%

Tensile Modulus
-- 2	2900	MPa	ASTM D638
--	2900	MPa	ISO 527-2/1
Tensile Strength
Yield 3	58.0	MPa	ASTM D638
Yield	58.0	MPa	ISO 527-2/50
Break 3	52.0	MPa	ASTM D638
Break	52.0	MPa	ISO 527-2/50
Tensile Elongation
Yield 3	7.0	%	ASTM D638
Yield	7.0	%	ISO 527-2/50
Break 3	12	%	ASTM D638
Break	12	%	ISO 527-2/50
Flexural Modulus
50.0 mm Span 4	2600	MPa	ASTM D790
-- 5	2600	MPa	ISO 178
Flexural Stress
-- 5, 6	95.0	MPa	ISO 178
Yield, 50.0 mm Span 4	95.0	MPa	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength 7 (23°C)	12	kJ/m2	ISO 179/1eA
Notched Izod Impact
-30°C	70	J/m	ASTM D256
23°C	100	J/m	ASTM D256
-30°C 8	7.0	kJ/m2	ISO 180/1A
23°C 8	10	kJ/m2	ISO 180/1A
Instrumented Dart Impact (23°C, Total Energy)	60.0	J	ASTM D3763

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed, 3.20 mm	195	°C	ASTM D648
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	191	°C	ISO 75-2/Bf