英力士INEOS Lustran ABS 732冰箱内衬
|
Density / Specific Gravity |
1.06 |
g/cm3 |
ASTM D792 |
|
Molding Shrinkage - Flow |
0.40 to 0.60 |
% |
ASTM D955 |
| Hardness |
Nominal Value |
Unit |
Test Method |
|
Rockwell Hardness (R-Scale) |
82 |
ASTM D785 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Modulus |
2300 |
MPa |
ASTM D638 |
|
Tensile Strength |
ASTM D638 | ||
|
Yield, 23°C |
22.8 |
MPa |
|
|
Break, 23°C |
28.3 |
MPa |
|
|
Tensile Elongation (Break) |
100 |
% |
ASTM D638 |
| Impact |
Nominal Value |
Unit |
Test Method |
|
Notched Izod Impact |
ASTM D256 | ||
|
-18°C |
75 |
J/m |
|
|
23°C |
200 |
J/m |
|
|
Instrumented Dart Impact |
ASTM D3763 | ||
|
Peak Force |
16.3 |
J |
|
|
Total Energy |
33.9 |
J |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Deflection Temperature Under Load (1.8 MPa, Annealed) |
87.8 |
°C |
ASTM D648 |
|
CLTE - Flow |
7.2E-5 |
cm/cm/°C |
ASTM D696 |
塑料ABS的热变形温度为93~118℃，制品经退火处理后还可提高10℃左右。ABS在-40℃时仍能表现出一定的韧性，可在-40~100℃的温度范围内使用。塑料ABS的电绝缘性较好，并且几乎不受温度、湿度和频率的影响，可在大多数环境下使用。
塑料ABS也可以说是聚苯乙烯的改性，比HIPS有较高的抗冲击强度和更好的机械强度，具有良好的加工性能，可以使用注塑机、挤出机等塑料成型设备进行注塑、挤塑、吹塑、压延、层合、发泡、热成型，还可以焊接、涂覆、电镀和机械加工。ABS的吸水性比较高，加工前需进行干燥处理，干燥温度为70~85℃，干燥时间为2~6h；ABS制品在加工中容易产生内应力，如应力太大，致使产品开裂，应进行退火处理，把制件放于70~80℃的热风循环干燥箱内2~4h，再冷却至室温即可。