ABS MAGNUM 8434
| General | |
|
Material Status
|
|
|
Availability
|
EuropeLatin AmericaNorth America |
|
Features
|
Good ProcessabilityHigh GlossHigh Heat ResistancePaintable |
|
Uses
|
AppliancesAutomotive ApplicationsAutomotive Interior PartsToys |
|
Automotive Specifications
|
|
|
Forms
|
|
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
g/cm3
|
ISO 1183 | |
|
Apparent (Bulk) Density
|
g/cm3
|
ISO 60 | |
|
Melt Mass-Flow Rate (MFR)(220°C/10.0 kg)
|
g/10 min
|
ISO 1133 | |
|
Molding Shrinkage
|
%
|
ISO 294-4 | |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
psi
|
ISO 527-2/1 | |
|
Tensile Stress(Yield)
|
psi
|
ISO 527-2/50 | |
|
Tensile Strain
|
ISO 527-2/50 | ||
|
Yield
|
%
|
||
|
Break
|
%
|
||
|
Flexural Modulus2
|
psi
|
ISO 178 | |
|
Flexural Stress2
|
psi
|
ISO 178 |
ABS MAGNUM 8434
成型性能
无定形材料,流动性中等,吸湿大,必须充分干燥,表面要求光泽的塑件须长时间预热干燥80-90度,3小时；
宜取高料温,高模温,但料温过高易分解(分解温度为270度).对精度较高的塑件,模温宜取50-60度,对高光泽.耐热塑件,模温宜取60-80度；
如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位等方法；
如成形耐热级或阻燃级材料，生产3-7天后模具表面会残存塑料分解物，导致模具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；
冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式浇口。模具宜加热，应选用耐磨钢；
料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过高易溢边，出现银丝暗条，塑件变色起泡；