| 品牌 | 旭化成 |
| 货号 | 300 |
| 用途 | 配件 |
| 牌号 | X531V |
| 型号 | X531V |
| 品名 | PPO |
| 外形尺寸 | 25/kg |
| 生产企业 | 旭化成 |
| 是否进口 | 否 |
| 加工/物理特性 | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ASTM数据(ASTM Data) | |||
| 模具收缩(Mold Shrinkage) (MD) | 0.003 | mm/mm | ASTM D 955 |
| 模具收缩(Mold Shrinkage) (TD) | 0.005 | mm/mm | ASTM D 955 |
| 密度(Density) (73°F) | 1150 | kg/m3 | ASTM D 792 |
| 机械性能(机械性能(Mechanical properties)) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据 | |||
| 屈服应力(Yield stress) | 71 | MPa | ISO 527-1/-2 |
| 断裂拉伸应变(Nominal strain at break) | 2 | % | ISO 527-1/-2 |
| 简支梁缺口冲击强度(Charpy notched impact strength) (+23°C) | 5 | kJ/m2 | ISO 179/1eA |
| 弯曲弹性模量(Flexural modulus) (23°C) | 3600 | MPa | ISO 178 |
| 热性能(热性能(Thermal properties)) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据 | |||
| 温度负荷变形(Temp. of deflection under load) (1.80 MPa) | 118 | °C | ISO 75-1/-2 |
| COEFF线性热(Coeff. of linear therm. expansion) (parallel) | 50.4 | E-6/K | ISO 11359-1/-2 |
| Burning behav. at 1.5 mm nom. thickn. | V-0 | class | IEC 60695-11-10 |
| 厚度测试(Thickness tested) | 1.6 | mm | IEC 60695-11-10 |
| Burning behav. 5V at thickness h | 5VA | class | IEC 60695-11-20 |
| 厚度测试(Thickness tested) | 2.5 | mm | IEC 60695-11-20 |
| ASTM数据(ASTM Data) | |||
| UL 94 阻燃等级(Flame rating) | V-0 | - | UL 94 |
| 厚度测试(Thickness tested) | 1.6 | mm | - |
| DTUL @ 264 psi | 120 | °C | ASTM D 648 |
| 电气性能(Electrical properties) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据 | |||
| 相对介电常数(Relative permittivity) (100Hz) | 3.1 | - | IEC 60250 |
| 相对介电常数(Relative permittivity) (1MHz) | 3 | - | IEC 60250 |
| 耗散因数(耗散因数(Dissipation factor)) (100Hz) | 30 | E-4 | IEC 60250 |
| 耗散因数(耗散因数(Dissipation factor)) (1MHz) | 50 | E-4 | IEC 60250 |
| 体积电阻率(Volume resistivity) | >1E13 | Ohm*m | IEC 60093 |
| 表面电阻率(Surface resistivity) | >1E15 | Ohm | IEC 60093 |
| 其他属性(Other properties) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ISO数据 | |||
| 吸水率(Water absorption) | 0.06 | % | Sim. to ISO 62 |
| 密度(Density) | 1150 | kg/m3 | ISO 1183 |