PA66物性表 Asahi Kasei尼龙66 Leona 1300G物性表
|
Asahi Kasei Leona? 1300G 33% Glass Filled（聚酰胺-尼龙66）
本物性表由中国塑商之家www.plas-cn.com塑料网提供，转载请注明来源！
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Specific Gravity比重
|
1.39g/cc
|
1.39g/cc
|
Dry; ASTM D792
|
|
Water Absorption吸水率
|
1.7 %
|
1.7 %
|
Wet
|
|
Linear Mold Shrinkage线性收缩率
|
0.0040cm/cm
|
0.0040in/in
|
Dry; ASTM D2863
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.0090cm/cm
|
0.0090in/in
|
Dry; ASTM D2863
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Hardness, Rockwell M罗氏硬度M
|
75
|
75
|
Wet; ASTM D785
|
|
96
|
96
|
Dry; ASTM D785
|
|
|
Hardness, Rockwell R罗氏硬度R
|
112
|
112
|
Wet; ASTM D785
|
|
120
|
120
|
Dry; ASTM D785
|
|
|
Tensile Strength, Yield屈服拉伸强度
|
132MPa
|
19100psi
|
Wet; ASTM D638
|
|
186MPa
|
27000psi
|
Dry; ASTM D638
|
|
|
Elongation at Break断裂伸长率
|
3.0 %
|
3.0 %
|
Dry; ASTM D638
|
|
5.0 %
|
5.0 %
|
Wet; ASTM D638
|
|
|
Flexural Strength弯曲强度
|
216MPa
|
31300psi
|
Wet; ASTM D790
|
|
289MPa
|
41900psi
|
Dry; ASTM D790
|
|
|
Flexural Modulus弯曲弹性模量
|
6.30GPa
|
914ksi
|
Wet; ASTM D790
|
|
9.30GPa
|
1350ksi
|
Dry; ASTM D790
|
|
|
Izod Impact, Notched悬臂梁缺口冲击强度
|
1.27J/cm
|
2.38ft-lb/in
|
Dry; ASTM D256
|
|
1.47J/cm
|
2.75ft-lb/in
|
Wet; ASTM D256
|
|
|
Taber Abrasion, mg/1000 Cycles周期泰伯磨耗
|
15
|
15
|
Wet; ASTM D1044
|
|
Thermal Properties热性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
CTE, linear线性热膨胀系数
|
30.0μm/m-°C@Temperature 20.0 °C
|
16.7μin/in-°F@Temperature 68.0 °F
|
Dry; ASTM D696
|
|
Specific Heat Capacity比热容
|
1.59J/g-°C
|
0.380BTU/lb-°F
|
Dry
|
|
Thermal Conductivity导热系数
|
0.300W/m-K
|
2.08BTU-in/hr-ft2-°F
|
Dry
|
|
Deflection Temperature at热变形温度0.46 MPa (66 psi)
|
260°C
|
500°F
|
Dry; ASTM D648
|
|
Deflection Temperature at热变形温度1.8 MPa (264 psi)
|
250°C
|
482°F
|
Dry; ASTM D648
|
|
Flammability, UL94阻燃等级
|
HB
|
HB
|
Dry
|
|
Oxygen Index氧指数
|
23 %
|
23 %
|
Dry; ASTM D2863
|
1300G是日本旭化成公司 聚酰胺树脂 尼龙66 型号之一,商品名Leona,是一种产量很高,品种最多,用途最广泛的 塑胶原料,具有优良的机械强度,优良的韧性,优秀的力学性能,优秀的自润滑性,优秀的耐摩性,优秀的电绝缘性,良好的耐热性,良好的耐气候性,广泛用于机械领域、汽车领域、电子电器领域、纺织行业、化工行业、航空冶金等领域。