全国咨询热线：13433004964
|
| 品牌 | 旭化成 |
| 货号 | 200 |
| 用途 | 配件 |
| 牌号 | FG170 |
| 型号 | FG170 |
| 品名 | PA66 |
| 外形尺寸 | 25/kg |
| 生产企业 | 旭化成 |
| 是否进口 | 否 |
日本旭化成15玻纤阻燃PA66 Leona FG170
FG170玻璃纤维含量为15% GF; 阻燃等级UL94 V-0。
|
Density / Specific Gravity |
1.48 |
-- |
g/cm3 |
ASTM D792, ISO 1183 |
|
Molding Shrinkage |
Internal Method | |||
|
Across Flow |
1.0 |
-- |
% |
|
|
Flow |
0.60 |
-- |
% |
|
Tensile Modulus (23°C) |
7500 |
5700 |
MPa |
ISO 527-2 |
|
Tensile Stress |
||||
|
Break, 23°C |
131 |
100 |
MPa |
ISO 527-2 |
|
-- |
132 |
108 |
MPa |
ASTM D638 |
|
Charpy Notched Impact Strength |
6.0 |
5.0 |
kJ/m2 |
ISO 179 |
|
Charpy Unnotched Impact Strength |
44 |
45 |
kJ/m2 |
ISO 179 |
|
Notched Izod Impact |
49 |
59 |
J/m |
ASTM D256 |
| Thermal |
Dry |
Conditioned |
Unit |
Test Method |
|
Deflection Temperature Under Load |
||||
|
0.45 MPa, Unannealed |
255 |
-- |
°C |
ASTM D648 |
|
0.45 MPa, Unannealed |
256 |
-- |
°C |
ISO 75-2/B |
|
1.8 MPa, Unannealed |
248 |
-- |
°C |
ASTM D648 |
|
1.8 MPa, Unannealed |
240 |
-- |
°C |
ISO 75-2/A |
|
Flame Rating (0.75 mm) |
V-0 |
-- |
UL 94 | |
|
Glow Wire Flammability Index (3.0 mm) |
960 |
-- |
°C |
IEC 60695-2-12 |
PA66特性
1、具有优良的 性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差
2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。
3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是 常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。
4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的较弱。