| 品牌 | 旭化成 |
| 货号 | 200 |
| 用途 | 配件 |
| 牌号 | 14G33 |
| 型号 | 14G33 |
| 品名 | PA66 |
| 外形尺寸 | 25/kg |
| 生产企业 | 旭化成 |
| 是否进口 | 否 |
PA66物性表 Asahi Kasei尼龙66 Leona 14G33物性表
|
Asahi Kasei Leona? 14G33 33% Glass Filled（聚酰胺-尼龙66）
本物性表由中国塑商之家www.plas-cn.com塑料网提供，转载请注明来源！
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Specific Gravity比重
|
1.39g/cc
|
1.39g/cc
|
Dry; ASTM D792
|
|
Water Absorption吸水率
|
1.7 %
|
1.7 %
|
Wet
|
|
Linear Mold Shrinkage线性收缩率
|
0.0040cm/cm
|
0.0040in/in
|
Dry; ASTM D2863
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.0080cm/cm
|
0.0080in/in
|
Dry; ASTM D2863
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Hardness, Rockwell M罗氏硬度M
|
75
|
75
|
Wet; ASTM D785
|
|
96
|
96
|
Dry; ASTM D785
|
|
|
Hardness, Rockwell R罗氏硬度R
|
120
|
120
|
Dry; ASTM D785
|
|
Tensile Strength, Yield屈服拉伸强度
|
135MPa
|
19600psi
|
Wet; ASTM D638
|
|
210MPa
|
30500psi
|
Dry; ASTM D638
|
|
|
Elongation at Break断裂伸长率
|
3.0 %
|
3.0 %
|
Dry; ASTM D638
|
|
5.0 %
|
5.0 %
|
Wet; ASTM D638
|
|
|
Flexural Strength弯曲强度
|
210MPa
|
30500psi
|
Wet; ASTM D790
|
|
325MPa
|
47100psi
|
Dry; ASTM D790
|
|
|
Flexural Modulus弯曲弹性模量
|
6.30GPa
|
914ksi
|
Wet; ASTM D790
|
|
10.4GPa
|
1510ksi
|
Dry; ASTM D790
|
|
|
Izod Impact, Notched悬臂梁缺口冲击强度
|
1.30J/cm
|
2.44ft-lb/in
|
Dry; ASTM D256
|
|
1.70J/cm
|
3.18ft-lb/in
|
Wet; ASTM D256
|
|
|
Taber Abrasion, mg/1000 Cycles周期泰伯磨耗
|
15
|
15
|
Wet; ASTM D1044
|
|
Thermal Properties热性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
CTE, linear线性热膨胀系数
|
20.0μm/m-°C@Temperature 20.0 °C
|
11.1μin/in-°F@Temperature 68.0 °F
|
Dry; ASTM D696
|
|
Thermal Conductivity导热系数
|
0.300W/m-K
|
2.08BTU-in/hr-ft2-°F
|
Dry
|
|
Deflection Temperature at热变形温度0.46 MPa (66 psi)
|
260°C
|
500°F
|
Dry; ASTM D648
|
|
Deflection Temperature at热变形温度1.8 MPa (264 psi)
|
250°C
|
482°F
|
Dry; ASTM D648
|
|
Flammability, UL94阻燃等级
|
HB
|
HB
|
Dry
|
14G33是日本旭化成公司 聚酰胺树脂 尼龙66 型号之一,商品名Leona,是一种产量很高,品种最多,用途最广泛的 塑胶原料,具有优良的机械强度,优良的韧性,优秀的力学性能,优秀的自润滑性,优秀的耐摩性,优秀的电绝缘性,良好的耐热性,良好的耐气候性,广泛用于机械领域、汽车领域、电子电器领域、纺织行业、化工行业、航空冶金等领域