| 品牌 | 瑞士EMS |
| 货号 | 100 |
| 用途 | 配件 |
| 牌号 | BG-50 FC |
| 型号 | BG-50 FC |
| 品名 | PA6 |
| 外形尺寸 | 25/kg |
| 生产企业 | 瑞士EMS |
| 是否进口 | 否 |
瑞士EMS高刚级50%GF/PA6 Grilon BG-50 FC
|
Density |
1.58 |
-- |
g/cm3 |
ISO 1183 |
|
Molding Shrinkage |
ISO 294-4 | |||
|
Across Flow |
0.50 |
-- |
% |
|
|
Flow |
0.10 |
-- |
% |
|
|
Water Absorption |
ISO 62 | |||
|
Saturation, 23°C |
5.0 |
-- |
% |
|
|
Equilibrium, 23°C, 50% RH |
1.5 |
-- |
% |
| Mechanical |
Dry |
Conditioned |
Unit |
Test Method |
|
Tensile Modulus |
17200 |
11500 |
MPa |
ISO 527-2 |
|
Tensile Stress (Break) |
240 |
155 |
MPa |
ISO 527-2 |
|
Tensile Strain (Break) |
3.0 |
6.0 |
% |
ISO 527-2 |
| Impact |
Dry |
Conditioned |
Unit |
Test Method |
|
Charpy Notched Impact Strength |
ISO 179/1eA | |||
|
-30°C |
11 |
12 |
kJ/m2 |
|
|
23°C |
15 |
25 |
kJ/m2 |
|
|
Charpy Unnotched Impact Strength |
ISO 179/1eU | |||
|
-30°C |
85 |
90 |
kJ/m2 |
|
|
23°C |
90 |
95 |
kJ/m2 |
| Thermal |
Dry |
Conditioned |
Unit |
Test Method |
|
Heat Deflection Temperature |
||||
|
1.8 MPa, Unannealed |
215 |
-- |
°C |
ISO 75-2/A |
|
8.0 MPa, Unannealed |
180 |
-- |
°C |
ISO 75-2/C |
|
Continuous Use Temperature |
||||
|
-- 3 |
100 to 120 |
-- |
°C |
ISO 2578 |
|
-- 4 |
200 |
-- |
°C |
Internal Method |
|
Melting Temperature 5 |
222 |
-- |
°C |
ISO 11357-3 |
| Flammability |
Dry |
Conditioned |
Test Method |
|
|
Flammability Classification (0.8 mm) |
HB |
-- |
IEC 60695-11-10, -20 |
PA6的化学物理特性和PA66很相似，然而，它的熔点较低，而且工艺温度范围很宽。它的抗冲击性和抗溶解性比PA66要好,但吸湿性也更强。因为塑件的许多品质特性都要受到吸湿性的影响，因此使用PA6设计产品时要充分考虑到这一点。为了提高PA6塑胶原料的机械特性，经常加入各种各样的改性剂。玻璃就是 常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。对于没有添加剂的产品，PA6的收缩率在1%到1.5%之间。成型组装的收缩率主要受材料结晶度和吸湿性影响。