高光泽 气味低DOW HDPE DMDA-8007 NT 7
- 价格： ￥10/千克
- 发布日期： 2023-09-21
- 更新日期： 2025-05-01
产品详请
| 品牌 |
陶氏
|
| 货号 |
300
|
| 用途 |
配件
|
| 特性级别 |
透明级|||热稳定性|||标准级|||耐磨|||高滑动|||高光泽|||
|
| 牌号 |
DMDA-8007 NT 7
|
| 型号 |
DMDA-8007 NT 7
|
| 加工级别 |
注塑级|||挤出级|||吹塑级|||吹膜级|||
|
| 品名 |
HDPE
|
| 外形尺寸 |
25/kg
|
| 用途级别 |
通用级|||管材级|||薄膜级|||家电部件|||
|
| 生产企业 |
陶氏
|
| 是否进口 |
否
|
陶氏高密度聚乙烯 DMDA-8007 NT 7High Density Polyethylene ResinThe Dow Chemical Company产品说明：Excellent stiffness/modulusExcellent warp resistanceMolded parts have high gloss, low odorFor injection molded crates, cases, totes, and other parts needing high modulusComplies with U.S. FDA 21 CFR 177.1520 (c)2.2Complies with Canadian HPFB No ObjectionComplies with EU, No 10/2011Consult the regulations for complete details.DOW DMDA-8007 NT 7 High Density Polyethylene (HDPE) Resin is a narrow molecular weight distribution high density homopolymer designed to offer excellent stiffness, low warpage, good/acceptable toughness, and good moldability. This resin is ideally suited for injection molded crates, cases, trays, tote bins, and other objects requiring high rigidity. This resin is also suitable for cast film extrusion processing.
陶氏高密度聚乙烯 DMDA-8007 NT 7 物性表
|
基本信息
|
|
机构评级
|
-
FDA 21 CFR 177.1520(c) 2.2
-
HPFB (加拿大) No Objection
-
欧洲 No 10/2011
|
|
形式
|
|
|
加工方法
|
|
|
物理性能
|
额定值
|
单位制
|
测试方法
|
|
比重
|
0.965
|
g/cm3
|
ASTM D792
|
|
熔流率（熔体流动速率）
|
ASTM D1238
|
|
190°C/2.16 kg
|
8.3
|
g/10 min
|
ASTM D1238
|
|
190°C/21.6 kg
|
180
|
g/10 min
|
ASTM D1238
|
|
抗环境应力开裂 1(50°C, 99.99% Igepal, F50)
|
2.00
|
hr
|
ASTM D1693
|
|
硬度
|
额定值
|
单位制
|
测试方法
|
|
肖氏硬度 2(邵氏 D)
|
61
|
ASTM D2240
|
|
机械性能
|
额定值
|
单位制
|
测试方法
|
|
抗张强度 3
|
ASTM D638
|
|
屈服
|
31.0
|
MPa
|
ASTM D638
|
|
断裂
|
17.9
|
MPa
|
ASTM D638
|
|
伸长率 4
|
ASTM D638
|
|
屈服
|
6.0
|
%
|
ASTM D638
|
|
断裂
|
350
|
%
|
ASTM D638
|
|
弯曲模量 - 2% 正割 5
|
1410
|
MPa
|
ASTM D790B
|
|
薄膜
|
额定值
|
单位制
|
测试方法
|
|
薄膜厚度 - 经测试
|
25
|
μm
|
|
膜耐刺穿性 (25 μm)
|
0.579
|
J/cm3
|
内部方法
|
|
割线模量
|
ASTM D882
|
|
2% 正割, MD : 25 μm, 铸造薄膜
|
798
|
MPa
|
ASTM D882
|
|
2% 正割, TD : 25 μm, 铸造薄膜
|
935
|
MPa
|
ASTM D882
|
|
抗张强度
|
ASTM D882
|
|
MD : 屈服, 25 μm, 挤塑薄膜
|
20.4
|
MPa
|
ASTM D882
|
|
TD : 屈服, 25 μm, 挤塑薄膜
|
22.4
|
MPa
|
ASTM D882
|
|
伸长率
|
ASTM D882
|
|
MD : 断裂, 25 μm, 挤塑薄膜
|
670
|
%
|
ASTM D882
|
|
TD : 断裂, 25 μm, 挤塑薄膜
|
490
|
%
|
ASTM D882
|
|
落锤冲击 (25 μm, 铸造薄膜)
|
24
|
g
|
ASTM D1709A
|
|
埃尔曼多夫抗撕强度
|
ASTM D1922
|
|
MD : 25 μm, 铸造薄膜
|
36
|
g
|
ASTM D1922
|
|
TD : 25 μm, 铸造薄膜
|
160
|
g
|
ASTM D1922
|
|
冲击性能
|
额定值
|
单位制
|
测试方法
|
|
拉伸冲击强度
|
168
|
kJ/m2
|
ASTM D1822
|
|
热性能
|
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度 6(0.45 MPa, 未退火)
|
83.9
|
°C
|
ASTM D648
|
|
脆化温度 7
|
< -76.1
|
°C
|
ASTM D746
|
|
维卡软化温度
|
131
|
°C
|
ASTM D1525
|
|
溶融温度（DSC）
|
133
|
°C
|
内部方法
|
|
结晶峰温度 (DSC)
|
120
|
°C
|
内部方法
|
|
光学性能
|
额定值
|
单位制
|
测试方法
|
|
光泽度 (45°, 25.4 μm, 铸造薄膜)
|
75
|
ASTM D2457
|
|
雾度 (25.4 μm, 铸造薄膜)
|
8.0
|
%
|
ASTM D1003
|