| 品牌 | 沙特基础 |
| 货号 | 100 |
| 用途 | 配件 |
| 牌号 | EFL-4036 UFE |
| 型号 | EFL-4036 UFE |
| 品名 | PEI |
| 外形尺寸 | 25/kg |
| 生产企业 | 沙特基础 |
| 是否进口 | 是 |
而头盔外壳是头盔的外层，在撞击时承受和分散冲击，是保护头部的 道防线
PEI 基础创新塑料(美国) EFL-4036 15%PTFE增强 注塑级
产品说明：
Features: Lubricated
Forms: Pellets
Processing Method: Injection Molding
Information provided by LNP, a GE Plastics Company.
This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
物理性能额定值 (公制)额定值 (英制)测试方法| 比重 | 1.62 g/cc | 1.62 g/cc | Method A; ASTM D792 |
| 密度 | 1.62 g/cc | 0.0585 lb/in3 | ISO 1183 |
| 吸水率 | 0.10 % | 0.10 % | at 24 hrs; ASTM D570 |
| 线性成型收缩率 | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| 线性成型收缩率，横向 | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| 抗张强度(断裂) | 161 MPa | 23400 psi | ASTM D638 |
| 伸长率 (断裂) | 2.1 % | 2.1 % | ASTM D638 |
| 拉伸模量 | 12.2 GPa | 1770 ksi | ASTM D638 |
| 弯曲强度 | 234 MPa | 33900 psi | ASTM D790 |
| 弯曲模量 | 11.1 GPa | 1610 ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 |
1.07 J/cm
@Thickness 3.18 mm |
2.00 ft-lb/in
@Thickness 0.125 in |
ASTM D256 |
| 悬壁梁无缺口冲击强度 |
5.50 J/cm
@Thickness 3.18 mm |
10.3 ft-lb/in
@Thickness 0.125 in |
ASTM D256 |
| 悬壁梁缺口冲击强度 | 17.4 kJ/m2 | 8.28 ft-lb/in2 | ISO 180 |
| 悬壁梁无缺口冲击强度 | 43.6 kJ/m2 | 20.7 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 9.60 J | 7.08 ft-lb | ASTM D3763 |
| 冲击试验 | 3.12 J | 2.30 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| 动态摩擦系数 | 0.46 | 0.46 | vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894 |
| 静态摩擦系数 | 0.43 | 0.43 | vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894 |
| K (wear) Factor | 70.5 x 10-8 mm3/N-M | 35.0 x 10-10 in3-min/ft-lb-hr | 40psi, 50ft/min; tested in accordance with LNP WI-0687 |
| 载荷下热变形温度(1.8 MPa) | 205 °C | 401 °F | Unannealed; ASTM D648 |
| 加工（熔体）温度 | 360 - 366 °C | 680 - 691 °F |
|
| 模具温度 | 121 - 149 °C | 250 - 300 °F |
|
| 干燥温度 | 121 - 149 °C | 250 - 300 °F |
|
| 干燥时间 | 4 hour | 4 hour |
|
| 水分含量 | 0.020 % | 0.020 % | Suggested |
| 背压 | 0.345 - 0.689 MPa | 50.0 - 99.9 psi |
|
PEI 基础创新塑料(美国) EFL-4036 15%PTFE增强 注塑级