韩国乐天ABS Starex SR-0330L高抗冲

Density / Specific Gravity (Natural)

1.07

g/cm3

ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)

3.5

g/10 min

ASTM D1238, ISO 1133
Molding Shrinkage

Flow : 3.20 mm

0.40 to 0.70

%

ASTM D955
Across Flow : 3.20 mm

0.40 to 0.70

%

ASTM D955
Across Flow : 2.00 mm

0.40 to 0.70

%

ISO 294-4
Flow : 2.00 mm

0.40 to 0.70

%

ISO 294-4
Hardness
Nominal Value

Unit

Test Method

Rockwell Hardness

R-Scale

115

ASTM D785
R-Scale

114

ISO 2039-2
Mechanical
Nominal Value

Unit

Test Method

Tensile Strength

Yield 2

51.0

MPa

ASTM D638
Yield

51.0

MPa

ISO 527-2/50
Break 2

49.0

MPa

ASTM D638
Break

48.0

MPa

ISO 527-2/50
Tensile Elongation

Break 2

17

%

ASTM D638
Break

17

%

ISO 527-2/50
Flexural Modulus

-- 3

2400

MPa

ASTM D790
-- 4

2400

MPa

ISO 178
Flexural Strength

-- 3

71.0

MPa

ASTM D790
-- 4

78.0

MPa

ISO 178
Impact
Nominal Value

Unit

Test Method

Charpy Notched Impact Strength 5 (23°C)

13

kJ/m2

ISO 179/1eA
Notched Izod Impact

23°C, 3.18 mm

140

J/m

ASTM D256
23°C, 6.35 mm

130

J/m

ASTM D256
-30°C 5

8.0

kJ/m2

ISO 180/1A
23°C 5

14

kJ/m2

ISO 180/1A
由于ABS有高的光泽和易成型性，办公室设备机器需要有漂亮的外观，有良好的手感，如电话机外壳、存储器外壳以及计算机、传真机、复印机中都大量使用了ABS制作的零件。

3、家用电器

由于ABS有高的光泽和易成型性，所以在家电和小家电中更有着 的市场，如家用传真机、音响、VCD中也大量 ABS为原料，吸尘器中也使用了很多ABS制作的零件，厨房用具也大量使用了ABS制作的零件。