韩国乐天ABS Starex VG-4920 20%玻纤阻燃

Density / Specific Gravity (Natural)

1.33

g/cm3

ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)

25

g/10 min

ASTM D1238, ISO 1133
Molding Shrinkage - Flow

3.20 mm

0.10 to 0.30

%

ASTM D955
2.00 mm

0.10 to 0.30

%

ISO 294-4
Hardness
Nominal Value

Unit

Test Method

Rockwell Hardness

R-Scale

110

ASTM D785
R-Scale

115

ISO 2039-2
Mechanical
Nominal Value

Unit

Test Method

Tensile Modulus

-- 3

5700

MPa

ASTM D638
--

6300

MPa

ISO 527-2/50
Tensile Strength

Yield 3

94.0

MPa

ASTM D638
Yield

100

MPa

ISO 527-2/50
Break 3

94.0

MPa

ASTM D638
Break

100

MPa

ISO 527-2/50
Tensile Elongation

Break 3

3.0

%

ASTM D638
Break

3.0

%

ISO 527-2/50
Flexural Modulus

-- 4

5900

MPa

ASTM D790
-- 5

7100

MPa

ISO 178
Flexural Strength

-- 4

100

MPa

ASTM D790
-- 5

130

MPa

ISO 178
Impact
Nominal Value

Unit

Test Method

Charpy Notched Impact Strength 6 (23°C)

7.0

kJ/m2

ISO 179/1eA
Notched Izod Impact

23°C, 3.18 mm

49

J/m

ASTM D256
23°C, 6.35 mm

49

J/m

ASTM D256
23°C 6

7.0

kJ/m2

ISO 180/1A
ABS树脂是五大合成树脂之一，其抗冲击性、耐热性、耐低温性、耐化学药品性及电气性能优良，还具有易加工、制品尺寸稳定、表面光泽性好等特点，容易涂装、着色，还可以进行表面喷镀金属、电镀、焊接、热压和粘接等二次加工， 应用于机械、汽车、电子电器、仪器仪表、纺织和建筑等工业领域，是一种用途极广的热塑性工程塑料。ABS通常为浅黄色或乳白色的粒料非结晶性树脂。ABS为使用 非通用塑料之一。