韩国乐天30%玻纤V1阻燃PC INFINO LS-3302L

Density / Specific Gravity (Natural)

1.41

g/cm3

ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) (250°C/10.0 kg)

13

g/10 min

ASTM D1238, ISO 1133
Molding Shrinkage

Flow : 3.20 mm

0.10 to 0.40

%

ASTM D955
Across Flow : 3.20 mm

0.30 to 0.60

%

ASTM D955
Across Flow : 2.00 mm

0.30 to 0.60

%

ISO 294-4
Flow : 2.00 mm

0.10 to 0.40

%

ISO 294-4
Ash Content

--

30

%

ASTM D5630
--

30

%

ISO 3451
Mechanical
Nominal Value

Unit

Test Method

Tensile Strength

Yield 2

120

MPa

ASTM D638
Yield

120

MPa

ISO 527-2/5
Break 2

120

MPa

ASTM D638
Break

120

MPa

ISO 527-2/5
Tensile Elongation

Break 2

3.5

%

ASTM D638
Break

3.5

%

ISO 527-2/5
Flexural Modulus

-- 3

7400

MPa

ASTM D790
-- 4

7400

MPa

ISO 178
Flexural Strength

-- 3

160

MPa

ASTM D790
-- 4

160

MPa

ISO 178
Impact
Nominal Value

Unit

Test Method

Charpy Notched Impact Strength 5 (23°C)

21

kJ/m2

ISO 179/1eA
Notched Izod Impact

23°C, 3.18 mm

160

J/m

ASTM D256
23°C, 6.35 mm

150

J/m

ASTM D256
23°C 5

20

kJ/m2

ISO 180/1A
Thermal
Nominal Value

Unit

Test Method

Deflection Temperature Under Load

1.8 MPa, Unannealed, 6.40 mm

140

°C

ASTM D648
1.8 MPa, Unannealed, 4.00 mm

140

°C

ISO 75-2/A
Flammability
Nominal Value

Test Method

Flame Rating

UL 94
0.8 mm

V-2

3.2 mm

V-1

 PC塑胶原料的吸水率较大，加工 定要预热干燥，纯PC干燥120℃，改性PC一般用110℃温度干燥4小时以上。干燥时间不能超过10小时。一般可用对空挤出法判断干燥是否足够。再生料的使用比例可达20%。在某些情况下，可 的使用再生料，实际份量要视制品的品质要求而定。再生料不能同时混合不同的色母粒，否则会严重损坏成品的性质。