| 品牌 | 乐天化学 |
| 货号 | 100 |
| 用途 | 配件 |
| 牌号 | QC-1220UR |
| 型号 | QC-1220UR |
| 品名 | PC |
| 外形尺寸 | 25/kg |
| 生产企业 | 乐天化学 |
| 是否进口 | 否 |
| 比重 | ASTM D792 | Natural 或代表 color | - | 1.20 |
| 熔融指数 | ASTM D1238 | 300℃, 1.2kg | g/10min | 22.0 |
| 成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.5~0.7 |
| 成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.5~0.7 |
| 机械性质 | ||||
|---|---|---|---|---|
| 拉伸强度(at yield) | ASTM D638 | 50mm/min | kgf/cm2 | 640 |
| 伸长率(at break) | ASTM D638 | 50mm/min | % | 110 |
| 拉伸模量23000 | ASTM D638 | 50mm/min | kgf/cm2 | 23000 |
| 断裂强度(at break) | ASTM D638 | 50mm/min | kgf/cm2 | 640 |
| 弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 920 |
| 弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 23000 |
| Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 10 |
| Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 75 |
| 硬度 | ASTM D785 | R-Scale | - | 120 |
| 热学特性 | ||||
|---|---|---|---|---|
| 热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 125 |
| 热变形温度 | ASTM D648 | 4.6kgf/cm2, 6.4mm | °C | 136 |
| 维卡软化温度 | ISO 306 | B/50 | °C | 145 |
| 阻燃 | ||||
|---|---|---|---|---|
| 阻燃度 | UL94 | V-2 | mm | 1.6~3.2 |
| 项目 | 单位 | 代表值 | ||
|---|---|---|---|---|
| 模具温度(Standard Molding) | 固定轴 | °C | 80 ~ 120 | |
| 移动轴 | ||||
| Hot Runner 温度 | Manifold | °C | 290 | |
| Valve nozzle | 300 | |||
| Nozzle温度 | °C | 300 | ||
| Cylinder温度 | 前端 | °C | 270 ~ 300 | |
| 中部 | 250 ~ 270 | |||
| 下部 | 50 ~ 80 | |||
| 注塑压力 | kgf/cm2 | 65 | ||
| 干燥条件 | 干燥方式 | 干燥温度 | °C | 120 |
| 干燥时间 | hr | 4 | ||
| 热风方式 | 干燥温度 | °C | 120 | |
| 干燥时间 | hr | 4 | ||
| 干燥后合适水分量 | % | < 0.05 | ||
| 计量速度 | rpm | 120 ~ 130 | ||
| 背压 | kgf/cm2 | 15 ~ 15 | ||