40%玻纤增强PPS LNP THERMOCOMP OFC08 SABIC
|
Density / Specific Gravity |
1.66 |
g/cm? |
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (315°C/5.0 kg) |
25 |
g/10 min |
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (315°C/5.0 kg) |
15 |
cm?/10min |
ISO 1133 |
|
Molding Shrinkage |
|
|
Internal Method |
|
Flow |
0.20 to 0.30 |
% |
|
|
Across Flow |
0.40 to 0.60 |
% |
|
|
Water Absorption |
|
|
|
|
24 hr, 23°C |
0.010 |
% |
ASTM D570 |
|
24 hr, 23°C |
0.020 |
% |
ISO 62 |
|
Saturation, 23°C |
0.030 |
% |
ISO 62 |
|
Equilibrium, 23°C, 50% RH 2 |
0.010 |
% |
ISO 62 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Modulus |
|
|
|
|
-- 3 |
16000 |
MPa |
ASTM D638 |
|
-- |
16000 |
MPa |
ISO 527-1/1 |
|
Tensile Strength |
|
|
|
|
Break 4 |
195 |
MPa |
ASTM D638 |
|
Break |
200 |
MPa |
ISO 527-2/5 |
|
Tensile Elongation |
|
|
|
|
Break 4 |
2.2 |
% |
ASTM D638 |
|
Break |
2.2 |
% |
ISO 527-2/5 |
|
Flexural Modulus |
|
|
|
|
50.0 mm Span 5 |
15300 |
MPa |
ASTM D790 |
|
-- 6 |
15000 |
MPa |
ISO 178 |
|
Flexural Strength |
|
|
|
|
50.0 mm Span 5 |
295 |
MPa |
ASTM D790 |
|
-- 6 |
295 |
MPa |
ISO 178 |
| Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength 7 (23°C) |
10 |
kJ/m? |
ISO 179/1eA |
|
Charpy Unnotched Impact Strength 7 (23°C) |
55 |
kJ/m? |
ISO 179/1eU |
|
Notched Izod Impact |
|
|
|
|
23°C |
100 |
J/m |
ASTM D256 |
|
-40°C 8 |
10 |
kJ/m? |
ISO 180/1A |
|
23°C 8 |
10 |
kJ/m? |
ISO 180/1A |
|
Unnotched Izod Impact |
|
|
|
|
23°C |
480 |
J/m |
ASTM D4812 |
|
-40°C 8 |
50 |
kJ/m? |
ISO 180/1U |
|
23°C 8 |
50 |
kJ/m? |
ISO 180/1U |