牌号
|
弯曲模量 (MPa)
|
% 填料/增强材料 (%)
|
简支梁缺口冲击强度 (kJ/m)
|
熔融体积流量（MVR） (cm/10min)
|
密度 (g/cm)
|
相比耐漏电起痕指数(CTI)
|
UL 阻燃等级
|
RTI Elec (°C)
|
RTI Imp (°C)
|
RTI (°C)
|
|
5010CTN33
|
8700 (2.0 mm/min)
|
33 (Unspecified)
|
5.0 (23°C)
|
16.0 (250°C/5.0 kg)
|
1.71
|
PLC 1
|
V-0 (0.75 mm)
|
75.0 (0.75 mm)
|
75.0 (0.75 mm)
|
75.0 (0.75 mm)
|
|
5010GN1-05 M
|
3250 (2.0 mm/min)
|
5.0 (Glass Fiber)
|
3.6 (23°C)
|
80.2 (250°C/5.0 kg)
|
1.47
|
PLC 3
|
V-0 (0.71 mm)
|
130 (0.71 mm)
|
120 (0.71 mm)
|
130 (0.71 mm)
|
|
5010GN1-15 AM
|
6200 (2.0 mm/min)
|
15 (Glass Fiber)
|
6.3 (23°C)
|
40.0 (250°C/5.0 kg)
|
1.54
|
PLC 3
|
V-0 (0.71 mm)
|
130 (0.71 mm)
|
120 (0.71 mm)
|
130 (0.71 mm)
|
|
5010GN1-15-8S
|
5400 (2.0 mm/min)
|
15 (Glass Fiber)
|
6.5 (23°C)
|
65.0 (250°C/5.0 kg)
|
1.52
|
PLC 3
|
V-0 (0.71 mm)
|
130 (0.71 mm)
|
130 (0.71 mm)
|
130 (0.71 mm)
|
|
5010GN1-20 AM
|
7200 (2.0 mm/min)
|
20 (Glass Fiber)
|
6.0 (23°C)
|
40.0 (250°C/5.0 kg)
|
1.58
|
PLC 3
|
V-0 (0.71 mm)
|
130 (0.71 mm)
|
120 (0.71 mm)
|
130 (0.71 mm)
|
|
5010GN1-30 AM
|
10200 (2.0 mm/min)
|
30 (Glass Fiber)
|
10 (23°C)
|
44.0 (250°C/5.0 kg)
|
1.68
|
PLC 3
|
V-0 (0.71 mm)
|
130 (0.71 mm)
|
120 (0.71 mm)
|
130 (0.71 mm)
|
|
5010GN1-30 AM2
|
10500 (2.0 mm/min)
|
30 (Glass Fiber)
|
10 (23°C)
|
30.0 (250°C/5.0 kg)
|
1.66
|
PLC 3
|
V-0 (0.71 mm)
|
130 (0.71 mm)
|
120 (0.71 mm)
|
130 (0.71 mm)
|
|
5010GN1-30 X4
|
10500 (2.0 mm/min)
|
30 (Glass Fiber)
|
8.3 (23°C)
|
30.0 (250°C/5.0 kg)
|
1.65
|
PLC 3
|
V-0 (0.71 mm)
|
130 (0.71 mm)
|
120 (0.71 mm)
|
130 (0.71 mm)
|
|
5010GN1-30NX1
|
8000 (2.0 mm/min)
|
30 (Glass Fiber)
|
7.0 (23°C)
|
35.0 (250°C/5.0 kg)
|
1.61
|
PLC 3
|
V-0 (0.71 mm)
|
140 (0.75 mm)
|
140 (0.75 mm)
|
140 (0.75 mm)
|
|
5010GN1-30TX2
|
8930 (2.0 mm/min)
|
30 (Glass Fiber)
|
11 (23°C)
|
24.0 (250°C/5.0 kg)
|
1.6
|
PLC 3
|
|
|
|
|
|
5010GN2-15
|
6400 (2.0 mm/min)
|
15 (Glass Fiber)
|
6.0 (23°C)
|
48.0 (250°C/5.0 kg)
|
1.54
|
PLC 3
|
V-0 (0.8 mm); V-0 (3.0 mm)
|
130 (0.8 mm)
|
120 (0.8 mm)
|
130 (0.8 mm)
|
|
5010GN2-30X2
|
10500 (2.0 mm/min)
|
30 (Glass Fiber)
|
9.0 (23°C)
|
45.0 (250°C/5.0 kg)
|
1.66
|
PLC 3
|
V-0 (0.8 mm); V-0 (1.5 mm); V-0 (3.0 mm); 5VA (1.5 mm); 5VA (3.0 mm)
|
140 (0.8 mm)
|
130 (0.8 mm)
|
140 (0.8 mm)
|
|
5010GN6-05
|
3800 (2.0 mm/min)
|
5.0 (Glass Fiber)
|
4.0 (23°C)
|
30.0 (250°C/5.0 kg)
|
1.47
|
PLC 3
|
V-0 (0.70 mm)
|
140 (0.75 mm)
|
130 (0.75 mm)
|
140 (0.75 mm)
|
|
5010GN6-15
|
5890 (2.0 mm/min)
|
15 (Glass Fiber)
|
4.0 (23°C)
|
62.0 (250°C/5.0 kg)
|
1.59
|
PLC 2
|
V-0 (0.75 mm)
|
130 (0.75 mm)
|
130 (0.75 mm)
|
140 (0.75 mm)
|
|
5010GN6-15M8 AM
|
6100 (2.0 mm/min)
|
15 (Glass Fiber)
|
7.0 (23°C)
|
62.0 (250°C/5.0 kg)
|
1.55
|
PLC 2
|
V-0 (0.75 mm)
|
130 (0.75 mm)
|
130 (0.75 mm)
|
140 (0.75 mm)
|
|
5010GN6-15M8 LT
|
6300 (2.0 mm/min)
|
15 (Glass Fiber)
|
4.0 (23°C)
|
38.0 (250°C/5.0 kg)
|
1.61
|
PLC 2
|
V-0 (0.75 mm)
|
130 (0.75 mm)
|
130 (0.75 mm)
|
140 (0.75 mm)
|
|
5010GN6-15M8X
|
6500 (2.0 mm/min)
|
15 (Glass Fiber)
|
6.8 (23°C)
|
25.9 (250°C/5.0 kg)
|
1.57
|
PLC 2
|
V-0 (0.30 mm); V-0 (1.5 mm); 5VA (1.5 mm)
|
130 (0.30 mm)
|
130 (0.30 mm)
|
140 (0.30 mm)
|
|
5010GN6-15T
|
5900 (2.0 mm/min)
|
15 (Glass Fiber)
|
8.0 (23°C)
|
46.0 (250°C/5.0 kg)
|
1.53
|
PLC 2
|
V-0 (0.75 mm)
|
130 (0.75 mm)
|
130 (0.75 mm)
|
140 (0.75 mm)
|
|
5010GN6-15TS
|
5900 (2.0 mm/min)
|
15 (Glass Fiber)
|
7.0 (23°C)
|
40.0 (250°C/5.0 kg)
|
1.52
|
PLC 2
|
V-0 (0.75 mm)
|
130 (0.71 mm)
|
130 (0.71 mm)
|
140 (0.71 mm)
|
|
5010GN6-20
|
7500 (2.0 mm/min)
|
20 (Glass Fiber)
|
8.0 (23°C)
|
25.0 (250°C/5.0 kg)
|
1.57
|
PLC 2
|
V-0 (0.75 mm)
|
130 (0.75 mm)
|
130 (0.75 mm)
|
140 (0.75 mm)
|
|
5010GN6-20M8 AM
|
6800 (2.0 mm/min)
|
20 (Glass Fiber)
|
8.0 (23°C)
|
50.0 (250°C/5.0 kg)
|
1.62
|
PLC 2
|
V-0 (0.38 mm)
|
75.0 (0.38 mm); 130 (0.75 mm)
|
75.0 (0.38 mm); 130 (0.75 mm)
|
75.0 (0.38 mm); 140 (0.75 mm)
|
|
5010GN6-20M8X
|
7900 (2.0 mm/min)
|
20 (Glass Fiber)
|
8.0 (23°C)
|
22.0 (250°C/5.0 kg)
|
1.62
|
PLC 2
|
V-0 (0.30 mm)
|
130 (0.75 mm)
|
130 (0.75 mm)
|
140 (0.75 mm)
|
|
5010GN6-20T
|
7300 (2.0 mm/min)
|
20 (Glass Fiber)
|
8.0 (23°C)
|
20.0 (250°C/5.0 kg)
|
1.57
|
PLC 2
|
V-0 (0.71 mm)
|
130 (0.71 mm)
|
130 (0.71 mm)
|
130 (0.71 mm)
|
|
5010GN6-30
|
10500 (2.0 mm/min)
|
30 (Glass Fiber)
|
10 (23°C)
|
50.0 (250°C/5.0 kg)
|
1.66
|
PLC 2
|
V-0 (0.38 mm); V-0 (0.76 mm)
|
130 (0.76 mm)
|
130 (0.76 mm)
|
140 (0.76 mm)
|
|
5010GN6-30M8AM
|
9410 (2.0 mm/min)
|
30 (Glass Fiber)
|
10 (23°C)
|
66.3 (250°C/5.0 kg)
|
1.7
|
PLC 2
|
V-0 (0.38 mm)
|
130 (0.38 mm)
|
130 (0.38 mm)
|
130 (0.38 mm)
|
|
5010GN6-30M8X
|
10500 (2.0 mm/min)
|
30 (Glass Fiber)
|
9.7 (23°C)
|
18.4 (250°C/5.0 kg)
|
1.71
|
PLC 2
|
V-0 (0.25 mm); V-0 (0.30 mm)
|
130 (0.30 mm)
|
130 (0.30 mm)
|
130 (0.30 mm)
|
|
5010GN6-30T
|
9900 (2.0 mm/min)
|
30 (Glass Fiber)
|
10 (23°C)
|
20.0 (250°C/5.0 kg)
|
1.64
|
PLC 2
|
V-0 (0.71 mm)
|
130 (0.71 mm)
|
130 (0.71 mm)
|
130 (0.71 mm)
|