Density / Specific Gravity

1.10

--

g/cm

Molding Shrinkage

Flow : 2.00 mm

0.90

--

%

Across Flow : 2.00 mm

0.90

--

%

Water Absorption

24 hr, 23°C

0.40

--

%

24 hr, 100°C

2.6

--

%

Dry

Conditioned

Unit

Test Method

Rockwell Hardness

M-Scale

65

--

R-Scale

--

110

Dry

Conditioned

Unit

Test Method

Tensile Strength(2.00 mm)

80.0

70.0

MPa

Tensile Elongation(Break, 2.00 mm)

50

50

%

Flexural Modulus

2400

2200

MPa

Flexural Strength

110

100

MPa

Dry

Conditioned

Unit

Test Method

Notched Izod Impact

200

220

J/m

Dry

Conditioned

Unit

Test Method

Deflection Temperature Under Load(1.8 MPa, Unannealed)

135

--

°C

Glass Transition Temperature

125

--

°C

Melting Temperature

320

--

°C

CLTE

Flow

8.0E-5

--

cm/cm/°C

Transverse

8.2E-5

--

cm/cm/°C