MECHANICAL

Tensile Stress, yld, Type I, 5 mm/min

400

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min

330

kgf/cm2

ASTM D 638

Tensile Strain, yld, Type I, 5 mm/min

2

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

25

%

ASTM D 638

Tensile Modulus, 5 mm/min

21700

kgf/cm2

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

630

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

21800

kgf/cm2

ASTM D 790

Tensile Stress, yield, 5 mm/min

38

MPa

ISO 527

Tensile Stress, break, 5 mm/min

31

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

2

%

ISO 527

Tensile Strain, break, 5 mm/min

25

%

ISO 527

Tensile Modulus, 1 mm/min

2260

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

61

MPa

ISO 178

Flexural Modulus, 2 mm/min

2140

MPa

ISO 178

IMPACT

Izod Impact, notched, 23°C

21

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

3

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

254

cm-kgf

ASTM D 3763

Izod Impact, notched 80*10*4 +23°C

16

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*4 -30°C

4

kJ/m2

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm

16

kJ/m2

ISO 179/1eA

THERMAL

Vicat Softening Temp, Rate B/50

98

°C

ASTM D 1525

HDT, 1.82 MPa, 3.2mm, unannealed

82

°C

ASTM D 648

CTE, -40°C to 40°C, flow

9.36E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

9.36E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, flow

9.36E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

9.36E-05

1/°C

ISO 11359-2

Vicat Softening Temp, Rate B/50

97

°C

ISO 306

Vicat Softening Temp, Rate B/120

101

°C

ISO 306

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

81

°C

ISO 75/Af

PHYSICAL

Specific Gravity

1.04

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.5 - 0.8

%

SABIC Method

Mold Shrinkage, xflow, 3.2 mm (5)

0.5 - 0.8

%

SABIC Method

Melt Flow Rate, 230°C/3.8 kgf

12

g/10 min

ASTM D 1238

Density

1.03

g/cm3

ISO 1183

Water Absorption, (23°C/sat)

1

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.2

%

ISO 62

Melt Volume Rate, MVR at 220°C/10.0 kg

40

cm3/10 min

ISO 1133

Injection Molding

Drying Temperature

80 - 90

°C

Drying Time

2 - 4

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0.01

%

Melt Temperature

205 - 245

°C

Nozzle Temperature

205 - 245

°C

Front - Zone 3 Temperature

205 - 225

°C

Middle - Zone 2 Temperature

200 - 210

°C

Rear - Zone 1 Temperature

190 - 200

°C

Mold Temperature

50 - 70

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

30 - 60

rpm

Shot to Cylinder Size

50 - 70

%

Vent Depth

0.038 - 0.051

mm