LATAMID 66 H2 G/50-GWHF1高流动50%玻纤PA66
|
Density |
1.58 |
g/cm |
ISO 1183 |
|
Molding Shrinkage2 |
|
|
ISO 294-4 |
|
Across Flow : 2.00 mm |
0.30 to 0.60 |
% |
|
|
Flow : 2.00 mm |
0.30 to 0.60 |
% |
|
|
Water Absorption(24 hr, 23°C) |
0.26 |
% |
ISO 62 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Modulus |
|
|
ISO 527-1/1 |
|
23°C |
16500 |
MPa |
|
|
60°C |
11000 |
MPa |
|
|
91°C |
6480 |
MPa |
|
|
121°C |
6000 |
MPa |
|
|
149°C |
4960 |
MPa |
|
|
Charpy Notched Impact Strength(23°C) |
12 |
kJ/m |
ISO 179/1eA |
|
Charpy Unnotched Impact Strength(23°C) |
64 |
kJ/m |
ISO 179/1eU |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Deflection Temperature Under Load |
|
|
|
|
0.45 MPa, Unannealed |
260 |
°C |
ISO 75-2/B |
|
1.8 MPa, Unannealed |
250 |
°C |
ISO 75-2/A |
|
Continuous Use Temperature3 |
135 |
°C |
ASTM E1641/E1877 |
|
Vicat Softening Temperature |
255 |
°C |
ISO 306/B50 |
|
CLTE - Flow(30 to 100°C) |
2.5E-5 |
cm/cm/°C |
ISO 11359-2 |
| Electrical |
Nominal Value |
Unit |
Test Method |
|
Surface Resistivity |
1.0E+12 |
ohms |
ASTM D257 |
|
Comparative Tracking Index4(Solution A) |
600 |
V |
IEC 60112 |