Density

1.36

g/cm

Molding Shrinkage2

Across Flow : 2.00 mm

0.40 to 0.60

%

Flow : 2.00 mm

0.40 to 0.60

%

Water Absorption(24 hr, 23°C)

0.34

%

Nominal Value

Unit

Test Method

Tensile Modulus

23°C

9310

MPa

60°C

6070

MPa

91°C

4620

MPa

121°C

3590

MPa

149°C

3170

MPa

Charpy Notched Impact Strength

-20°C

6.4

kJ/m

23°C

9.3

kJ/m

Charpy Unnotched Impact Strength

-30°C

64

kJ/m

-20°C

62

kJ/m

23°C

59

kJ/m

Nominal Value

Unit

Test Method

Deflection Temperature Under Load

0.45 MPa, Unannealed

220

°C

1.8 MPa, Unannealed

200

°C

Continuous Use Temperature3

100

°C

Vicat Softening Temperature

215

°C

CLTE - Flow(30 to 100°C)

3.5E-5

cm/cm/°C