| 品牌 | 威格斯 |
| 货号 | 100 |
| 用途 | 配件 |
| 牌号 | 150GL20 |
| 型号 | 150GL20 |
| 品名 | PEEK |
| 包装规格 | 25/KG |
| 外形尺寸 | 25/kg |
| 生产企业 | 威格斯 |
| 是否进口 | 否 |
Victrex PEEK VICOTE PEEK 701
Victrex PEEK VICOTE PEEK 702
Victrex PEEK VICOTE PEEK 703
Victrex PEEK VICOTE PEEK 704
Victrex PEEK VICOTE PEEK 705 Blue
Victrex PEEK VICOTE PEEK 705
Victrex PEEK VICOTE PEEK 705Blk
Victrex PEEK VICOTE PEEK 706
Victrex PEEK VICOTE PEEK 707
Victrex PEEK VICOTE PEEK 708
Victrex PEEK VICOTE PEEK 709
Victrex PEEK VICOTE PEEK F804
Victrex PEEK VICOTE PEEK F804Blk
Victrex PEEK VICOTE PEEK F805 Natural
Victrex PEEK VICOTE PEEK F806 Natural
Victrex PEEK VICOTE PEEK F807 Grey
Victrex PEEK VICOTE PEEK F807Blk
Victrex PEEK VICOTE PEEK F808 Natural
Victrex PEEK VICOTE PEEK F809 Natural
Victrex PEEK VICOTE PEEK F810 Grey
Victrex PEEK VICOTE PEEK F810Blk
Victrex PEEK VICOTE PEEK F813Blk
Victrex PEEK VICOTE PEEK F814
Victrex PEEK VICOTE PEEK F815
Victrex PEEK VICOTE PEEK F816Blk
Victrex PEEK VICOTE PEEK F817 Enhanced
聚醚醚酮属于聚醚酮类塑料中主要品种，在这个聚合物的重复单元中有两个醚键和酮基与苯环交互连构成线型大分子，故命名为聚醚醚酮，简称PEEK，PEEK是一种耐高温的结晶型热塑性工程材料。其合成方法主要有两种，一种通过酚盐与卤代芳径进行亲核取代反应；另一种是通过芳香酰氯或酸与芳径进行亲电取代反应。聚芳醚酮由于分子链中含有刚性的苯环结构，因此结晶温度很高。
PEEK是芳杂环聚合物中却是比较晚获得商品化的一个品种。英国帝国化学公司（LCL）的Victrex PEEK在1978年才投放到市场。虽然各公司开发了许多聚醚酮品种，其中最主要的品种仍然是聚醚醚酮。
PEEK具有高耐热性（纤维增强后其热变形温度在300℃）、耐热性（可在200~260℃蒸汽中使用）、耐疲劳性（是热塑性塑料中 的）耐腐蚀性（除浓硫酸和浓硝酸外无溶剂能侵蚀它）、耐腐蚀及阻燃性、机械强度及电绝缘好等特点。
|
添加剂 |
|
|
性能特点 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.37 |
g/cm3 |
ASTM D792, ISO 1183 |
|
收缩率 |
|||
|
流动 : 24小时 |
1.3 |
% |
ASTM D955 |
|
横向流动 : 24小时 |
1.9 |
% |
ASTM D955 |
|
横向流量 : 24小时 |
1.9 |
% |
ISO 294-4 |
|
流量 : 24小时 |
1.3 |
% |
ISO 294-4 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|||
|
-- 2 |
2900 |
MPa |
ASTM D638 |
|
-- |
3070 |
MPa |
ISO 527-2/1 |
|
抗张强度 |
|||
|
屈服 |
74.5 |
MPa |
ASTM D638 |
|
屈服 |
73.0 |
MPa |
ISO 527-2 |
|
断裂 |
69.6 |
MPa |
ASTM D638 |
|
断裂 |
69.0 |
MPa |
ISO 527-2 |
|
伸长率 |
|||
|
屈服 |
5.8 |
% |
ASTM D638 |
|
屈服 |
5.0 |
% |
ISO 527-2 |
|
断裂 |
23 |
% |
ASTM D638 |
|
断裂 |
12 |
% |
ISO 527-2 |
|
弯曲模量 |
|||
|
-- |
2960 |
MPa |
ASTM D790 |
|
-- |
3320 |
MPa |
ISO 178 |
|
弯曲强度 |
|||
|
-- |
117 |
MPa |
ASTM D790 |
|
-- |
118 |
MPa |
ISO 178 |
|
摩擦系数 |
ASTM D3702 Modified | ||
|
与自身 - 动态 |
0.52 |
|
|
|
与自身 - 静态 |
0.43 |
|
|
|
磨损因数 - Washer |
128 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|||
|
23°C |
96 |
J/m |
ASTM D256 |
|
23°C 3 |
8.8 |
kJ/m2 |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|||
|
23°C |
1500 |
J/m |
ASTM D4812 |
|
23°C 3 |
91 |
kJ/m2 |
ISO 180/1U |
|
装有测量仪表的落镖冲击 |
|||
|
23°C, Energy at Peak Load |
3.00 |
J |
ASTM D3763 |
|
-- |
1.00 |
J |
ISO 6603-2 |