| GENERAL | |
| Material Status |
Commercial: Active
|
| Search for UL Yellow Card |
GLOBAL POLYACETAL CO., LTD.
Reny™
|
| Availability |
Africa & Middle East
Asia Pacific
Europe
Latin America
North America
|
| Filler / Reinforcement |
Glass Fiber, 50% Filler by Weight
|
| Features |
Good Weather Resistance
Light Stabilized
|
| Uses |
Automotive Applications
Automotive Electronics
Electrical/Electronic Applications
General Purpose
|
| PHYSICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Density |
1.63
|
--
|
g/cm3
|
ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) |
1.6
|
--
|
g/10 min
|
ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) |
1.1
|
--
|
cm3/10min
|
ISO 1133 |
| Molding Shrinkage 2 | Internal Method | |||
| Across Flow : 130°C, 2.00 mm |
0.60
|
--
|
%
|
|
| Flow : 130°C, 2.00 mm |
0.30
|
--
|
%
|
|
| Water Absorption | Internal Method | |||
| 24 hr, 23°C |
0.14
|
--
|
%
|
|
| Equilibrium, 23°C, 50% RH |
0.80
|
--
|
%
|
| MECHANICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Modulus |
18700
|
17200
|
MPa
|
ISO 527-1/1 |
| Tensile Stress (Break) |
227
|
197
|
MPa
|
ISO 527-2/5 |
| Tensile Strain (Break) |
1.6
|
1.7
|
%
|
ISO 527-2/5 |
| Flexural Modulus 3 |
18300
|
15900
|
MPa
|
ISO 178 |
| Flexural Stress 3 |
329
|
292
|
MPa
|
ISO 178 |
| IMPACT |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength (23°C) |
9.0
|
9.2
|
kJ/m2
|
ISO 179 |
| Charpy Unnotched Impact Strength (23°C) |
45
|
45
|
kJ/m2
|
ISO 179 |
| THERMAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed |
233
|
231
|
°C
|
ISO 75-2/B |
| 1.8 MPa, Unannealed |
221
|
215
|
°C
|
ISO 75-2/A |
| ADDITIONAL INFORMATION | ||||
|
Conditioned
|
Conditioned to 50% RH
|
|||
| INJECTION |
Dry
|
Unit
|
|
| Drying Temperature | |||
| Hot Air Dryer, A |
120
|
°C
|
|
| Hot Air Dryer, B |
80
|
°C
|
|
| Drying Time | |||
| Hot Air Dryer, A |
> 3.0
|
hr
|
|
| Hot Air Dryer, B |
> 12
|
hr
|
|
| Rear Temperature |
265
|
°C
|
|
| Middle Temperature |
270
|
°C
|
|
| Front Temperature |
275
|
°C
|
|
| Nozzle Temperature |
275
|
°C
|
|
| Mold Temperature |
120 to 140
|
°C
|
|
| Injection Pressure |
20.0 to 150
|
MPa
|
|
| Injection Rate |
Moderate-Fast
|
|
|
| Screw Speed |
60 to 150
|
rpm
|