品牌 | 沙特基础 |
货号 | 100 |
用途 | 配件 |
牌号 | 15T1030 |
型号 | 15T1030 |
品名 | PP |
生产企业 | 沙特基础 |
特性级别 | 增强级|||高刚性||| |
加工级别 | 注塑级||| |
包装规格 | 25/KG |
外形尺寸 | 25/kg |
用途级别 | 通用级|||电动工具配件||| |
是否进口 | 否 |
SABIC PPcompound 15T1030高模量30%TD增强
Density | 1.15 | g/cm? | *** 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | *** 1133 |
Molding Shrinkage 1 (24 hr, 3.20 mm) | 1.1 | % | Internal Method |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (Injection Molded) | 3200 | MPa | *** 527-1/1A |
Tensile Stress | | | *** 527-2/1A |
Yield, Injection Molded | 32.5 | MPa | |
Break, Injection Molded | 25.0 | MPa | |
Tensile Strain (Break, Injection Molded) | 15 | % | *** 527-2/1A |
Flexural Modulus 2 (Injection Molded) | 3500 | MPa | *** 178 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C, Injection Molded) | 3.0 | kJ/m? | *** 179/1eA |
Notched Izod Impact Strength | | | *** 180/1A |
-20°C, Injection Molded | 2.0 | kJ/m? | |
0°C, Injection Molded | 2.5 | kJ/m? | |
23°C, Injection Molded | 3.0 | kJ/m? | |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load 3 (0.45 MPa, Unannealed) | 125 | °C | *** 75-2/B |
Vicat Softening Temperature 3 | 150 | °C | *** 306/A |
CLTE - Flow | | | |
-30 to 30°C | 5.0E-5 | cm/cm/°C | ASTM D696 |
23 to 80°C | 9.0E-5 | cm/cm/°C | ASTM D696 |
-30 to 100°C | 6.8E-5 | cm/cm/°C | *** 11359-2 |
Additional Information | Nominal Value | Unit | Test Method |
Filler Content | 30 | % | Internal Method |