全国咨询热线：13433004964
|
| 品牌 | 杜邦 |
| 货号 | 100 |
| 用途 | 配件 |
| 牌号 | 100ALE |
| 型号 | 100ALE |
| 品名 | POM |
| 外形尺寸 | 25/kg |
| 生产企业 | 美国杜邦 |
| 是否进口 | 是 |
美国杜邦超脱模级POM Delrin 100ALE
|
Density |
1.40 |
g/cm3 |
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) |
2.5 |
g/10 min |
ISO 1133 |
|
Molding Shrinkage |
ISO 294-4 | ||
|
Across Flow |
1.7 |
% |
|
|
Flow |
2.0 |
% |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Modulus |
3000 |
MPa |
ISO 527-2 |
|
Tensile Stress (Yield) |
70.0 |
MPa |
ISO 527-2 |
|
Tensile Strain (Yield) |
18 |
% |
ISO 527-2 |
|
Nominal Tensile Strain at Break |
40 |
% |
ISO 527-2 |
|
Poisson&＃39;s Ratio |
0.37 |
||
| Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30°C |
8.0 |
kJ/m2 |
|
|
23°C |
11 |
kJ/m2 |
|
|
Charpy Unnotched Impact Strength |
ISO 179/1eU | ||
|
-30°C |
200 |
kJ/m2 |
|
|
23°C |
No Break |
||
|
Notched Izod Impact Strength (23°C) |
8.0 |
kJ/m2 |
ISO 180/1A |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Melting Temperature 2 |
178 |
°C |
ISO 11357-3 |
|
Annealing Temperature |
160 |
°C |
|
|
Annealing Time - Optional |
30.0 |
min/mm |
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。
POM具有特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
POM是一种坚韧有弹性的材料，即使在低温下仍有很好的抗蠕变特性、几何稳定性和抗冲击特性。
POM的高结晶程度导致它有相当高的收缩率，可高达到2%~3.5%。对于各种不同的增强型材料有不同的收缩率。
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。