Density |
1.41 |
g/cm3 |
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) |
27 |
g/10 min |
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) |
23 |
cm3/10min |
ISO 1133 |
|
Molding Shrinkage - Flow (3.00 mm) |
2.0 |
% |
Internal Method |
|
Water Absorption - 60% RH (23°C) |
0.22 |
% |
Internal Method |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Modulus |
2900 |
MPa |
ISO 527-2/1 |
|
Tensile Stress (Yield) |
64.0 |
MPa |
ISO 527-2/50 |
|
Tensile Strain |
ISO 527-2/50 | ||
|
Yield |
7.5 |
% |
|
|
Break |
26 |
% |
|
|
Flexural Modulus 3 |
2700 |
MPa |
ISO 178 |
|
Flexural Stress 3 |
91.0 |
MPa |
ISO 178 |
| Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength (23°C) |
6.0 |
kJ/m2 |
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C) |
150 |
kJ/m2 |
ISO 179 |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Heat Deflection Temperature |
|||
|
0.45 MPa, Unannealed |
156 |
°C |
ISO 75-2/B |
|
1.8 MPa, Unannealed |
100 |
°C |
ISO 75-2/A |
|
Melting Temperature |
166 |
°C |
ISO 11357-3 |
| Flammability |
Nominal Value |
Test Method |
|
|
Flame Rating (0.8 mm) |
HB |
UL 94 |